Product NO.Tr-Fe-TiC
CategoryCarbide
PaymentT/T,Western Union
Inquiry Contact Us

Product Description

Specifications:

Purity:High purity
Size:80mesh,200mesh,44um or customized
Colour:Black

chemical composition/%


T I

C

SI

P

S

AL

CU

MN

FE

FeTiC30A

28-31

4.5-6.5

4.50

0.05

0.03

8.00

0.40

2.50


FeTiC30B

28-31

4.5-6.5

5.0

0.06

0.04

8.50

0.40

2.00


FeTiC40A

38-41

6.5-9.5

4.50

0.05

0.03

8.00

0.40

2.50


FeTiC40B

38-41

6.5-9.5

1.50

0.03

0.03

5.00

0.40

0.25


FeTiC40C

38-41

6.5-9.5

0.50

0.02

0.02

4.50

0.20

0.25


FeTiC70 A

68-71

12-15

1.50

0.03

0.03

5.00

0.20

0.30


FeTiC70B

68-71

12-15

1.00

0.03

0.03

4.50

0.20

0.25


FeTiC70C

68-71

12-15

0.50

0.02

0.02

3.00

0.20

0.25


 

Fe Titanium Carbide relative atomic weight 59.91, carbon 20.05%, density 4.93 g/cm 3, melting point 3160 , boiling point 4300 .Gray powder, has the NaCl type structure of cubic crystal system.Due to its high melting point, high hardness, good chemical stability, are mainly used for manufacturing metal ceramic, heat-resistant alloy and hard alloy.In WC - Co cemented carbide with 6 ~ 30% TiC, and WC form TiC - WC solid solution, can obviously improve the alloy's red heat resistance, abrasion resistance, oxidation resistance, corrosion resistance, such as performance, more than the WC - Co carbide is suitable for processing steel.Can also use Ni - Mo alloy as binder made from tungsten carbide, can improve the cutting speed and the precision of the machined part, finish.
Fe soft pure iron, but if it is an alloy of iron and other metal or is mixed with the impurities of iron, reduce the melting point and hardness will be increased, depending on the nature of the impurities or alloy.
TiC and Fe have their respective advantages and disadvantages, and Fe - TiC synthesis solved these problems, combined with the advantages of both, is a weak magnetic black powder.And more widely applied.

Application:
Titanium carbide and tungsten carbide, tantalum carbide, niobium carbide, chromium carbide, titanium nitride formation of binary, ternary and quaternary compound solid solution, used in coating material, welding materials, hard thin film materials, aviation material, cemented carbide and cermet, and have higher request for magnetic or toughness of the process.Titanium carbide, chemical formula of TiC, relative atomic weight of 59.91, the theory of carbon 20.05%, density of 4.93 g/cm 3, melting point 3160 , boiling point 4300 .Gray powder, has the NaCl type structure of cubic crystal system.Due to its high melting point, high hardness, good chemical stability, are mainly used for manufacturing metal ceramic, heat-resistant alloy and hard alloy.In WC - Co cemented carbide with 6 ~ 30% TiC, and WC form TiC - WC solid solution, can obviously improve the alloy's red heat resistance, abrasion resistance, oxidation resistance, corrosion resistance, such as performance, more than the WC - Co carbide is suitable for processing steel.Can also use Ni - Mo alloy as binder made from tungsten carbide, can improve the cutting speed and the precision of the machined part, finish.
Fe soft pure iron, but if it is an alloy of iron and other metal or is mixed with the impurities of iron, reduce the melting point and hardness will be increased, depending on the nature of the impurities or alloy.
TiC and Fe have their respective advantages and disadvantages, and Fe - TiC synthesis solved these problems, combined with the advantages of both, is a weak magnetic black powder.And more widely applied.